Material

FASHMO™ and CHAMUDE® are "man made leather": They both are materials that have the aesthetic and functional characteristics of genuine nubuck and suede leather. In fact, the structure of these two materials is comparable to human skin. They consist of superfine microfibre bundles, which in turn are embedded in billions of microfine pores. This creates a silky, finely ground surface. The high-tech microfibre of the man made leather has the highest quality standards and is certified according to Öko-Tex guidelines.

Fashmo™

FASHMO™ is made on the basis of nylon. Finest polyamide microfibers are twirled together and then soaked in a synthetic resin. The textile is finely sanded and brushed with a machine specially made for this process. This procedure creates a surface that is virtually indistinguishable from real suede leather.
In addition, the material is extremely easy to clean, can be machine washed, dries extremely fast, is breathable and tearproof. It is up to 30 percent lighter than real leather.

Characteristics and datasheets

DS 05

CHARACTERISTIC	UNIT	DEFAULT	VALUES
Material composition	%		70 Nylon/ 30 Polyurethan
Broad	cm		min.137
Weight	gr/m2	ASTM D3776	ca.160 +/- 25
Thickness	mm	ASTM D1117	ca. 0,53 +/- 0,05
Roll length	m		60
Tear strength	kg/cm	ASTM D5035	5,0 +/- 2 x 4,0 +/- 2
Elongation at break l x c/l x q	%	ASTM D5035	70 +/- 25% x 115 +/- 30%
Tear strength l x c/l x q	kg	ASTM D2261	70 +/- 25% x 115 +/- 30%
Color fastness to light	blue scale \| Blauskala	ISO 105B02	3
Color fastness to washing change/staining	grey scale \| Grauskala	ISO105C06	3-4 / 2-3
Color fastness on cleaning change/staining	grey scale \| Grauskala	ISO 105D01	4
Color fastness to dry/wet abrasion	grey scale \| Grauskala	ISO 105X12	3 / 2-3

Data sheet as PDF

DS 07

CHARACTERISTIC	UNIT	DEFAULT	VALUES
Material composition	%		60 Nylon / 40 Polyurethan
Broad	cm		min. 137
Weight	gr/m²	FZ/T 60003-1991	ca. 280 + 40
Thickness	mm	GB/T 8948-2008	ca. 0,7 + 0,05
Roll length	m		60
Tensile strenght	1N/cm	GB/T 1040.3-2006	≥ 35
Elongation at break l/w	%	GB/T 1040.3-2006	≥ 40
Tear strength	N	GB/T 8948-2008	black ≥ 16 / Others ≥ 22
Bursting pressure	kg/cm³	GB/T 1539-1989	≥ 10
Softness	mm	IUP/36	≥ 4
Color fastness to washing (Black color)	level	GB/T3921-2008	4
Color fastness to washing (Other colors)	level	GB/T3921-2008	4
Wear resistance	Cycles	ASTM D3884-01 (2007)	black ≥ 700 / Others ≥ 800
Fastness to rubbing dry	level	GB/T3920-2008	≥ 3-4 (black) / ≥ 2-3 (others)
Fastness to rubbing wet	level	GB/T3920-2008	≥ 2-3 (black) / ≥ 1-2 (others)

Data sheet as PDF

DS 10

CHARACTERISTIC	UNIT	DEFAULT	VALUES
Material composition	%		60 Nylon/ 40 Polyurethan
Fineness of the fiber	den	Denier System	0,001 ~ 0,05
Thickness	mm	GB/T 8948-2008	ca. 0,9 ~ 1,1
Broad	cm		> 137
Weight	gr/m²	FZ/T 60003-1991	ca. 420 + 50
Tensile strenght	1N/cm	GB/T 1040.3-2006	≥ 70
Elongation at break l/w	%	GB/T 1040.3-2006	≥ 35
Tear strength	N	GB/T 8948-2008	black ≥ 25 / others ≥ 28
Bursting pressure	kg/cm³	GB/T 1539-1989	≥ 15
Softness	mm	IUP/36	≥ 4
Wear resistance	Cycles	ASTM D3884-01	black ≥ 700 / Others ≥ 800
PH value			7 + 2
Fastness to rubbing dry	Greyscale	GB/T3920-2008	≥ 3-4 (black) / ≥ 2-3 (others)
Fastness to rubbing wet	Greyscale		≥ 2-3 (black) / ≥ 1-2 (others)
Color fastness in washing	Greyscale		black 4 / others 2-4

Data sheet as PDF

DS 12

CHARACTERISTIC	UNIT	DEFAULT	VALUES
Material composition	%		60 Nylon/ 40 Polyurethan
Broad	cm		min.137
Weight	gr/m2	ASTM D3776	ca.400 +/- 30
Thickness	mm	ASTM D1117	ca. 1,2 + 0,05
Roll length	m		30
Tear strength	kg/cm	ASTM D5035	17,0 +/- 5×15,5 +/- 5
Elongation at break l x c/l x q	%	ASTM D5035	90 +/- 25% x 110 +/- 25%
Tear strength l x c/l x q	kg	ASTM D2261	6,5 +/- 3×5,5 +/- 2
Color fastness to light	blue scale \| Blauskala	ISO 105B02	3
Color fastness to washing change/staining	grey scale \| Grauskala	ISO105C06	3-4 / 2-3
Color fastness on cleaning change/staining	grey scale \| Grauskala	ISO 105D01	4
Color fastness to dry/wet abrasion	gray scale \| Grauskala	ISO 105X12	3 / 2-3

Data sheet as PDF

DS 14

CHARACTERISTIC	UNIT	DEFAULT	VALUES
Material composition	%		60 Nylon/ 40 Polyurethan
Fineness of the fiber	den	Denier System	0,001 ~ 0,05
Thickness	mm	GB/T 8948-2008	ca. 1,3 ~ 1,5
Broad	cm		> 137
Weight	gr/m²	FZ/T 60003-1991	ca. 590 +/- 50
Tensile strenght	1N/cm	GB/T 1040.3-2006	≥ 85
Elongation at break l/w	%	GB/T 1040.3-2006	≥ 45
Tear strength	N	GB/T 8948-2008	black ≥ 35 / others ≥ 40
Bursting pressure	kg/cm³	GB/T 1539-1989	≥ 20
Softness	mm	IUP/36	≥ 3,5
Wear resistance	Cycles	ASTM D3884-01	black ≥ 700 / Others ≥ 800
PH value			7 +/- 2
Fastness to rubbing dry	Greyscale	GB/T3920-2008	≥ 3-4 (black) / ≥ 2-3 (others)
Fastness to rubbing wet	Greyscale	GB/T3920-2008	≥ 2-3 (black) / ≥ 1-2 (others)
Color fastness in washing	Greyscale	GB/T3920-2008	black 4 / others 2-4

Data sheet as PDF

Chamude^®

CHAMUDE® is the premium version of the innovative man made leather. The basis is a polyester fiber that can be produced in different thicknesses and colors and offers various possibilities for individual processing and finishing.

Characteristics and datasheets

DS 08

CHARACTERISTIC	UNIT	DEFAULT	VALUES
Material composition	%	ISO 1833	70 Polyester/ 30 Polyurethan
Broad	cm		min.139
Weight	gr/m2	ASTM D3776	ca. 270 +/- 30gr
Thickness	mm	ASTM D1777	ca. 0,95 +/- 0,06
Tear strength	kgf/cm	ASTM D5035	warp 8,0 +/- 3 weft 8,0 +/- 3
Elongation at break l x c/l x q	%	ASTM D5035	warp 50 +/- 15 weft 70 +/- 20
Tear strength l x c/l x q	kgf	ASTM D2261	warp 2,0 ↑ weft 2,0 ↑
Pilling (Martindale)	1.000 cycles 5.000 cycles 10.000 cycles	ISO 12945-1	4,5
Color fastness to light	blue scale \| Blauskala	ISO 105E04	3,5 ↑
Color fastness to washing change/staining	grey scale \| Grauskala	ISO105C06	3,5 ↑
Color fastness when wet	grey scale \| Grauskala	ISO 105E01	3,5 ↑
Color fastness to dry/wet abrasion	grey scale \| Grauskala	ISO 105X12	3,5 ↑ / 3,5 ↑

Data sheet as PDF

DS 11

CHARACTERISTIC	UNIT	DEFAULT	VALUES
Material composition	%	ISO 1833	70 Polyester/ 30 Polyurethan
Broad	cm		min.139
Weight	gr/m2	ASTM D3776	ca. 395 +/- 30gr
Thickness	mm	ASTM D1777	ca. 1,1 +/- 0,05
Tear strength	kgf/cm	ASTM D5035	warp 10,0 +/- 3 weft 11,0 +/- 3
Elongation at break l x c/l x q	%	ASTM D5035	warp90 +/- 25 weft80 +/- 25
Tear strength l x c/l x q	kgf	ASTM D2261	warp4,0 +/- 2 weft 3,5 +/- 1,5
Pilling (Martindale)	1.000 cycles 5.000 cycles 10.000 cycles	ISO 12945-1	4,5
Color fastness to light	blue scale \| Blauskala	ISO 105E04	3,0 ↑
Color fastness to washing change/staining	grey scale \| Grauskala	ISO105C06	3,0 ↑
Color fastness when wet	grey scale \| Grauskala	ISO 105E01	3,0 ↑
Color fastness to dry/wet abrasion	grey scale \| Grauskala	ISO 105X12	3,0 ↑ / 3,0 ↑

Data sheet as PDF

CHARACTERISTIC	UNIT	DEFAULT	VALUES
Material composition	%		70 Nylon/ 30 Polyurethan
Broad	cm		min.137
Weight	gr/m2	ASTM D3776	ca.160 +/- 25
Thickness	mm	ASTM D1117	ca. 0,53 +/- 0,05
Roll length	m		60
Tear strength	kg/cm	ASTM D5035	5,0 +/- 2 x 4,0 +/- 2
Elongation at break l x c/l x q	%	ASTM D5035	70 +/- 25% x 115 +/- 30%
Tear strength l x c/l x q	kg	ASTM D2261	70 +/- 25% x 115 +/- 30%
Color fastness to light	blue scale \| Blauskala	ISO 105B02	3
Color fastness to washing change/staining	grey scale \| Grauskala	ISO105C06	3-4 / 2-3
Color fastness on cleaning change/staining	grey scale \| Grauskala	ISO 105D01	4
Color fastness to dry/wet abrasion	grey scale \| Grauskala	ISO 105X12	3 / 2-3

Material

Fashmo™

Characteristics and datasheets

DS 05

DS 07

DS 10

DS 12

DS 14

Chamude^®

Characteristics and datasheets

DS 08

DS 11

Robust functional materials for fashion, sport and leisure

Links

Links

DS 05

Material

Fashmo™

Characteristics and datasheets

Chamude®

Characteristics and datasheets